| Cobalt (Co) | 63 |
|---|---|
| Cromo (Cr) | 28 |
| Niobio (Nb) | 4 |
| Tungsteno (W) | 3 |
| Altri (Mn, Fe, Si) | – |
DESCRIPTION
Type 4 in accordance with ISO 22674
Excellent flowability, allowing dental technicians to cast even large quantities of alloy with maximum precision in every part of the restoration
Low melting point and very low solidus-liquidus temperature compared to standard cobalt-chromium alloys
Clear oxidation, good workability, easy polishing.
Can also be used for creating bars and counter bars.
PHYSICAL CHARACTERISTICS
| Solidus-liquidus temperature | 1253 ÷ 1304 °C |
| Coefficient of thermal expansion | (25 ÷ 500 °C) 14.1 x 10-6 K-1 – (25 ÷ 600 °C) 14.5 x 10-6 K-1 |
| Melting point | 1360°C |
| Density | 8.4 g/cmc |
| Vickers hardness | 324 HV10 |
| Percentage elongation at break | 3 % |
| Unit yield strength | (Rp0.2) 475 MPa |
| Modulus of elasticity | 194 GPa |
| Jone release in 7 days | 0.8 μg/cm2 |
| Maximum firing temperature | 950°C |
| Colour | White |
CONFEZIONE
0123 ACCORDING TO: ISO 9693, ISO 22674